17-4 PH/ AISI630 Stainles Properties



Product  : 17-4PH Stainless Steel
Kategori : Martensitic Precipitation Hardening Stainless Steel
Standard: AFNOR
Grades   : 17-4PH

Equivalents

ASTM A693 grade 630, AISI 630, AMS 5604B, UNS S17400, EURONORM 1.4542, X5CrNiCuNb 16-4, AFNOR Z5 CNU 17-4PH, DIN 1.4542, JIS SUS630, SAE AMS 5643, SAE AMS 5604, NACE MR01-75, ISO 15156, PED 97/23/CE, API 6A PSL4 (UT), ASTM A388 (UT), EN10088-3

Characteristic

Stainless 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 300°C / 572°F) and corrosion resistance. It has good fabricating characteristics and can be age hardened.  Best machinability quality is in solution P 800 (H1150M) and P930 (H 1150)
Stainless 17-4 PH should not be used at temperatures above 300°C (572°F) or at very low temperatures. It has adequate resistance to atmospheric corrosion or in diluted acids or salts where its corrosion resistance is equivalent to grade 304 or 430.
Stainless 17-4 PH withstands corrosive attack better than any of the 400 series hardenable stainless steel, and in most applications, it's corrosion resistance closely approaches that of Stainless Types 303 and 304.


Availability

Roundbar


Chemical Composition (%)

 C Si Mn P S Cr Ni Cu Nb Mo
 0.04 Max 0.40 Max  0.80 Max 0.040 Max  0.030 Max 15.00-17.50 3.00-5.00 3.00-5.00 0.15-0.45  0.50 Max 
PREN (%Cr+3.3%Mo+16%N) ≥17


Mechanical Properties

Heat treatment YS 0.2%
N/mm_
UTS
N.mm_
YS 0.2%
ksi
UTS
ksi
EI%
Min. Typ. Min. Typ. Min. Typ. Min. Typ. Min. Typ.
A 1070 1207 1170 1310 155 175 170 190 8 14
B 790 931 965 1034 115 135 140 150 10 17

A: hardening 496°C (925°F) - 4 hours - air cooling
B: hardening 593°C (1100°F) - 4 hours - air cooling
2 examples of heat treatments that may be applied.
Tensile strength at delivery form approx 800-110 N/mm2
Very high yield strength up to 1100-1300 MPa (160-190 ksi) can be achieved.

Elevated temperature properties
Minimum guaranteed values following EN 10088 hot rolled plates.
The EN guaranteed values are valid for a thickness from 3/16" up to 3".

   Temperature °C
   Temperature °F
100
212
150
302
200
392
250
482
300
572
YS 0.2%N/mm_730710690670650
ksi1061031009795

Heat treatment : hardening 590°C (1094°F) - 4 hours - air cooling.
1 example of heat treatments that may be applied

Impact Values

Minimum guaranteed values following ASTM A693 hot rolled plates.
The ASTM guaranteed values are valid for a thickness from 3/16" up to 3".
Heat treatmentKV transverse
Jft.lbf
Hardening 593°C (1100°F) - 4 hours - air cooling 20 15

Hardness

Minimum guaranteed values following ASTM A693 hot rolled plates.
The ASTM guaranteed values are valid for a thickness from 3/16" up to 3".
Heat treatment Hardness
Rockwell Brinell
Hardening 496°C (925°F) - 4 hours - air cooling C38 375
Hardening 593°C (1100°F) - 4 hours - air cooling C29 293


Corrosion Resistance

Stainless 17-4 PH withstands corrosive attacks better than any of the standard hardenable stainless steels and is comparable to type 304 in most media.

If there are potential risks of stress corrosion cracking, the higher aging temperatures then must be selected over 550°C (1022°F), preferably 590°C (1094°F). 550°C-1022°F is the optimum tempering temperature in chloride media.

590°C-1094°F is the optimum tempering temperature in H2S media.

17-4 PH is subject to crevice or pitting attack if exposed to stagnant seawater for any length of time.

It is corrosion resistant in some chemical, petroleum, paper, dairy and food processing industries (equivalent to 304L grade).


Physical Properties

Have been obtained after hardening 480°C (896°F) – 1 hour - air cooling.
Interval
Temperature
°C
Thermal
expansion
ax10-6°C-1
°C °F Thermal
conductivity
(W.m-1.K-1)
Young
modulus
(GPa)
0-100 10.8 20 68 14 197
0-200 11 100 212 16 193
0-300 11.3 200 392 18.5 186
0-400 11.6 300 572 20 180
0-500 12 400 752 22 175
500 932 23 170


Properties (Room temp)
17-4PH
Resistivity (µ_.cm) 80
Specific heat (J.kg-1.K-1) 460
Tension modulus (GPa) 77
Density kg/m3 (.28 lbs/in3) 7800


Heat Treatment
Hardening condition P800 or P930 has to be solution annealed before hardening Max obtainable hardness 44 HRC (for more details please turn over)
Martensitic transformation
Indicative values
Ms : 130°C (266°F)
Mf : 30°C (86°F)
Solution annealing
1050°C +/-25°C (1925°F+ /-50°F) – 30 min up to 1 hour.
air cooling / oil quenching below 25°C (76°F)

Tempering
The highest mechanical properties are obtained with the following heat treatment: 480°C (896°F) – 1 hour – air cooling.
Higher ductilities are obtained when using higher aging temperatures up to 620°C (1148°F).

Applications

Offshore (foils, helicopter deck platforms, etc.)
Food industry
Pulp and paper industry.
Aerospace (turbine blades, etc.)
Mechanical components
Nuclear waste barrel
Parts used in Chemical process
Parts used in Mechanical process
Aircraft & gas turbines
Paper mills & oil fields

Source:
"The effect of microstructural evolution on hardening behavior of type 17-4PH stainless steel in long-term aging at 350 °C" Jun Wanga, b, Hong Zoub, Cong Lib, Shao-yu Qiub, Bao-luo Shena
a School of Materials Science and Engineering, Sichuan University, Chengdu, 610065, PR China
b Nuclear Power Institute of China, Chengdu, 610041, PR China

"Improving the mechanical properties of 17-4PH stainless steel by low temperature plasma surface treatment" M.F. Yan *, R.L. Liu, D.L. Wu
* School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, PR China

http://www.sandmeyersteel.com/17-4PH-spec.html
http://www.quantumalloys.com/data/ground/cro17-4.html
http://ntrs.nasa.gov/archive/nasa/casi.ntrs.nasa.gov/20070034041.pdf
http://www.sciencedirect.com/


Related Steel:

Incoming Search Terms: jual 17-4PH stainless, material 17-4ph, baja aisi 630, stainless precipitation, stainless steel aisi630 di jakarta,suplier 17-4ph, martensitic stainless 17-4ph, steel 17-4ph, stainless 17-4ph datasheet, equivalen aisi630 steel, mechanical properties 17-4ph,physical properties aisi630,UNS S17400 steel properties, baja UNS S17400, baja DIN 1.4542

Produk Terkait:

Tags:
  • Jual Plat,Hardox,Bisalloy,Creusabro,XAR,Brinar,Sumihard,Ympress,JFE Everhard, Fora,Corten,Harga Baja,jual stainless steel,304/L, 316, 310, 3Cr12, Durinox,201,Java Steel Pipe,distributor,Master,KS, GG, wear plate, jual steel,harga steel,JIS,SNI, ASTM,grade,400,500,daftar harga, 2012,jual besi baja,Aluminium,Nabalseventh,80, 4800, Harga besi, inp, cnp,unp,WF,H-beam,besi beton,besi cor,Steel AISI,valve, harga,Plate, Boiler,flange,Plat Kapal,SS400,A36,BKI,bisplate,SPCC,SPHC,Mild steel, Spesifikasi,pagar besi, toko besi, ASTM A516 gr.70,SM490-YA /YB, ABS, abrasion,Marine,Offshore Plates,DNV,standard,tabel,bolt,nuts,berat